陈志周,牟建楼,刘玮佳,于志彬,孙兰芳.纳米SiO2改性生物降解复合薄膜研究[J].包装工程,2019,40(3):86-93.
CHEN Zhi-zhou,MOU Jian-lou,LIU Wei-jia,YU Zhi-bin,SUN Lan-fang.Nano SiO2 Modified Biodegradable Composite Films.Packaging Engineering,2019,40(3):86-93.
纳米SiO2改性生物降解复合薄膜研究
Nano SiO2 Modified Biodegradable Composite Films
投稿时间:2018-10-14  修订日期:2019-02-10
DOI:10.19554/j.cnki.1001-3563.2019.03.012
中文关键词: 纳米SiO2  壳聚糖  木薯淀粉  聚乙烯醇(PVA)  生物降解
英文关键词: nano-SiO2  chitosan  cassava starch  polyvinyl alcohol (PVA)  biodegradation
基金项目:河北省科技计划(17227117D);河北省食品科学与工程学科“双一流”建设资金项目(2016SPGCA18)
作者单位
陈志周 河北农业大学 食品科技学院保定 071001 
牟建楼 河北农业大学 食品科技学院保定 071001 
刘玮佳 河北农业大学 食品科技学院保定 071001 
于志彬 河北农业大学 食品科技学院保定 071001 
孙兰芳 河北农业大学 食品科技学院保定 071001 
摘要点击次数: 111
全文下载次数: 126
中文摘要:
      目的 以壳聚糖(chitosan)、木薯淀粉和聚乙烯醇(PVA)为基础成膜原料,探究纳米SiO2改性木薯淀粉/PVA/壳聚糖薄膜的制备工艺过程。方法 以薄膜断裂伸长率、抗张强度、透光率和吸水率为评判标准,在单因子试验基础上,设计L9(34)正交试验,研究纳米SiO2含量、分散剂十二烷基苯磺酸含量、膜液pH值等3个因素对纳米SiO2改性木薯淀粉/聚乙烯醇/壳聚糖薄膜性能的影响。结果 得出了制备纳米SiO2改性木薯淀粉/PVA/壳聚糖薄膜的最佳工艺参数,纳米SiO2质量分数为2.0%、十二烷基苯磺酸钠质量分数为2.0%、膜液pH值为3.0,3个因素对改性薄膜性能的影响程度大小排序为分散剂含量>纳米SiO2含量>pH值。结论 获得了纳米SiO2改性木薯淀粉/PVA/壳聚糖薄膜的最佳生产工艺参数。
英文摘要:
      The work aims to study the preparation technology process of Nano-SiO2 modified cassava starch/ PVA/chitosan film, with chitosan, cassava starch and polyvinyl alcohol (PVA) as basic film-forming materials. With elongation at break, tensile strength, transmittance and water absorption as evaluation index, based on single factor test, the influences of the Nano-SiO2 content, the content of dispersant SDBS and the pH value of casing solution on properties of Nano-SiO2 modified cassava starch/PVA/chitosan films were studied through the design of L9 (34) orthogonal experiment. The best process parameters for the preparation of Nano-SiO2 modified cassava starch/PVA/chitosan film were obtained. The mass fraction of Nano-SiO2 was 2.0%, the mass fraction of SDBS was 2.0%, and the pH value of casting solution was 3.0. The ranking of three factors affecting the modified film performance was dispersant content>Nano-SiO2 content>pH value. The best production process parameters of Nano-SiO2 modified cassava starch/PVA/chitosan films are obtained.