赵鹏飞,张平平,刘晓丽,黄凯,叶壮志,刘亚男.曲面喷墨打印水性墨水研究[J].包装工程,2019,40(1):228-232.
ZHAO Peng-fei,ZHANG Ping-ping,LIU Xiao-li,HUANG kai,YE Zhuang-zhi,LIU Ya-nan.Water-based Ink for the Curved-surface Ink-jet Printing.Packaging Engineering,2019,40(1):228-232.
曲面喷墨打印水性墨水研究
Water-based Ink for the Curved-surface Ink-jet Printing
投稿时间:2018-08-17  修订日期:2019-01-10
DOI:10.19554/j.cnki.1001-3563.2019.01.033
中文关键词: 喷墨打印  水性墨水  曲面
英文关键词: ink-jet printing  water-based ink  curved surface
基金项目:北京市科技计划(Z171100002417025)
作者单位
赵鹏飞 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
张平平 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
刘晓丽 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
黄凯 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
叶壮志 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
刘亚男 1.中国印刷科学技术研究院北京 1000362. 印刷环保技术重点实验室北京 1000363. 包装印刷新技术北京市重点实验室北京 100036 
摘要点击次数: 200
全文下载次数: 171
中文摘要:
      目的 研究开发曲面喷墨打印水性喷墨墨水的制备,用喷墨打印的方式对不规则曲面制品进行图文装饰。方法 通过选择树脂种类,调整色浆和水的含量以及添加其他助剂,制备出具有较好印刷适性(如不堵塞喷头,粘度适宜,表面张力好)的水性喷墨墨水。结果 制备出的水性软性喷墨墨水和硬性喷墨墨水,软性墨水的颗粒度为0.2~0.6 μm,粘度控制在5~6 mPa?s,表面张力为27~29 mN/m;硬性墨水的颗粒度为0.3~0.6 μm,粘度控制在7~8 mPa?s,表面张力为25~27 mN/m。结论 通过对树脂种类、色浆的选择,水的含量及其他助剂的确定,制得了一款环保的曲面喷墨打印水性墨水。
英文摘要:
      The work aims to study and develop the preparation of water-based ink-jet ink for curved-surface ink-jet printing, and decorate the irregular curved-surface products with graphics and text by means of ink-jet printing. Through the selection of resin type, adjustment of the content of color paste and water and addition of other additives, the water-based ink-jet ink with better printability (such as no blockage of the nozzle, proper viscosity and good surface tension) was prepared. For the prepared water-based soft ink-jet ink and hard ink-jet ink, the particle size of the soft ink was 0.2~0.6 μm, the viscosity was controlled at 5~6 mPa?s, and the surface tension was 27~29 mN/m; while the particle size of the hard ink was 0.3~0.6 μm, the viscosity was controlled at 7~8 mPa?s, and the surface tension was 25~27 mN/m. Through the selection of resin type and color paste, and the determination of water content and other additives, an environmentally friendly water-based ink for curved-surface ink-jet printing is prepared.