苏绮钿,向华,蔡绵,黎佩影,简丹凤,林木雄,张炜斌.一种透明荧光防伪印油的研制[J].包装工程,2017,38(15):207-212.
SU Qi-tian,XIANG Hua,CAI Mian,LI Pei-ying,JIAN Dan-feng,LIN Mu-xiong,ZHANG Wei-bin.Development of Transparent Fluorescent Anti-counterfeiting Stamp-Ink[J].Packaging Engineering,2017,38(15):207-212.
一种透明荧光防伪印油的研制
Development of Transparent Fluorescent Anti-counterfeiting Stamp-Ink
投稿时间:2016-12-30  修订日期:2017-08-10
DOI:
中文关键词: 稀土基荧光粉  防伪  印油  透明  塑料薄膜
英文关键词: fluorescent powders based on rare earth  anti-counterfeiting  stamp-ink  transparent  plastic film
基金项目:国家自然科学基金(21601037);广东省自然科学基金(2014A030313692);制浆造纸工程国家重点实验室开放基金(201519);惠州市产学研结合项目(2014B050013020);广东轻工职业技术学院创新强校项目(2A10505,1A20601,1A20201)
作者单位
苏绮钿 广东轻工职业技术学院广州 510300 
向华 1.广东轻工职业技术学院广州 5103002.华南理工大学广州 5106403.佛山市防伪工程技术研究中心佛山 528225 
蔡绵 广东轻工职业技术学院广州 510300 
黎佩影 广东轻工职业技术学院广州 510300 
简丹凤 广东轻工职业技术学院广州 510300 
林木雄 广东轻工职业技术学院广州 510300 
张炜斌 1.广东轻工职业技术学院广州 5103002.佛山市防伪工程技术研究中心佛山 528225 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 获得一种透明荧光防伪印油的优选配方和制备步骤,并研究影响其物理指标和防伪指标的因素。方法 采用自制稀土基荧光粉,制备了一系列用于塑料薄膜的透明荧光防伪印油样品,通过研究树脂、荧光粉、芥酸酰胺(EA)和370M质量分数对印油印记物理指标——干燥性、抗反粘、附着牢度和防伪指标荧光性的影响,筛选出一种优化配方,并与同类某进口产品(市场样)进行比较研究。结果 树脂分子有助于提高荧光粉的发光强度;EA和370M有助于改善3个物理指标;EA和370M最优质量分数为1.5%。所得优选印油比市场样干燥快25%,负重抗反粘性比市场样提高了48%,附着牢度与市场样接近;印记透明,隐蔽性强,具有完全不同于市场样的防伪特征,表现出对检测波长的选择性,防伪力度优于市场样,耐光性5级,远高于市场样1级。结论 所得优选印油的各项指标综合表现优于同类进口产品,可望用于烟、酒和化妆品等高端产品外层的透明塑料薄膜上进行防伪。
英文摘要:
      To obtain an optimum formula and steps of a transparent fluorescent anti-counterfeiting stamp-ink and study factors affecting its physical and anti-counterfeiting indicators. A series of anti-counterfeiting stamp-inks for plastic films were prepared with self-made fluorescent powders based on rare earth. The effects of the contents of resin, fluorescent powders (EA) and 370M on the drying, blocking resistance, adhesion and fluorescence properties of imprinted samples were investigated in order to screen out an optimum formula whose properties were compared with those of a imported product (market sample). The resin molecule could increase the intensity of luminescent powders, while EA and 370M could improve the three physical properties. The best mass fraction of EA and 370M was 1.5%. The drying rate of the optimum stamp-ink was 25% faster than that of the counterpart, while its blocking resistance was 48% higher than that of the counterpart. Its adhesion strength was similar to that of the counterpart. The imprinted sample was transparent. It had high invisibility and anti-counterfeiting property very different to that of the counterpart. It showed the selection on the measure wavelength. Its anti-counterfeiting property was also superior to that of the counterpart. Its grade of light resistance was V which was I grade higher than that of the counterpart. The overall performance of the optimum formula is better than the counterpart, which might apply to the transparent plastic films outside packing materials of cigarette, alcohol and cosmetics to guard against falsification.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20817437位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号