王全亮,肖生苓,岳金权,陆新宗.重载纤维模塑材料热压成型的水分传递过程[J].包装工程,2017,38(9):96-101.
WANG Quan-liang,XIAO Sheng-ling,YUE Jin-quan,LU Xin-zong.Moisture Transfer Process of Hot-Press Molding of Overloaded Molded Fiber Material[J].Packaging Engineering,2017,38(9):96-101.
重载纤维模塑材料热压成型的水分传递过程
Moisture Transfer Process of Hot-Press Molding of Overloaded Molded Fiber Material
投稿时间:2016-10-03  修订日期:2017-05-10
DOI:
中文关键词: 重载  纤维模塑  热压成型  水分传递  水分分布
英文关键词: overloaded  molded fiber  hot-press molding  moisture transfer  water distribution
基金项目:中央高校基本科研业务费专项(2572016AB69);国家林业公益性行业科研专项(201304506)
作者单位
王全亮 东北林业大学哈尔滨 150040 
肖生苓 东北林业大学哈尔滨 150040 
岳金权 东北林业大学哈尔滨 150040 
陆新宗 东北林业大学哈尔滨 150040 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 探究各工艺因素(热压温度、热压压力、初始含水率、定量)对重载纤维模塑材料水分传递过程的影响,揭示重载纤维模塑材料热压成型的水分传递机理。方法 采用隔层设计测得纤维模塑板坯不同位置的水分变化;引入t 检验与F 检验法检验对称位置水分变化曲线的差异。结果 热压过程中,水分在重载纤维模塑板坯中对称分布,水分变化可划分为2 个阶段,即快速下降段(Q 段)和集中汽化段(L 段)。水分梯度主要发生在L 段,其水分传递依次满足菲克第一定律的稳态扩散和菲克第二定律的非稳态扩散,扩散速率由表及里逐渐减慢。在Q 段与L 段,提高热压温度、增大热压压力或减小定量均能加快芯层水分下降速率,初始水分含量对水分下降速率无明显影响。结论 热压过程中,重载纤维模塑材料由表及里先后完成干燥。降低初始含水率、提高热压温度、增大热压压力或减小定量均能缩短重载纤维模塑材料的干燥时长。
英文摘要:
      The work aims to study the effects of various process factors (hot-press temperature, hot-press pressure, and initial water content and basis weight) on the moisture transfer process of overloaded molded fiber material, and reveal the mechanism of moisture transfer in hot-press molding. The moisture change of molded fiber slab at different positions was measured in the method of interlayer design. The T test and F test methods were introduced to test the difference of water change curves at symmetrical position. During the hot-press process, the moisture content was symmetrically distributed in overloaded molded fiber materials and the moisture change could be divided into 2 stages: the rapid descending section (section Q) and the centralized vaporization section (section L). The moisture gradient mainly occurred in section L and its moisture transfer in turn met the steady state diffusion of Fick's first law and the unsteady state diffusion of Fick's second law. The diffusion rate gradually decreased from the outside to the inside. In sections Q and L, the increased hot-press temperature and pressure or the decreased basis weight could accelerate the descending rate of the moisture content of the core layer. The initial moisture content had no significant effect on the descending rate of moisture content. In hot-press process, the overloaded molded fiber material is dried from the outside to the inside. Reducing initial moisture content, improving hot-press temperature and pressure, or decreasing basis weight can shorten the drying time of overloaded molded fiber material.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20813457位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号