江向东,徐朝阳,李健昱.静态径向加载速率对樟子松吸能特性的影响[J].包装工程,2016,37(11):16-19.
JIANG Xiang-dong,XU Zhao-yang,LI Jian-yu.Impact of Radial Static Loading Rate on the Scotch Pine Energy Absorption Characteristics[J].Packaging Engineering,2016,37(11):16-19.
静态径向加载速率对樟子松吸能特性的影响
Impact of Radial Static Loading Rate on the Scotch Pine Energy Absorption Characteristics
投稿时间:2015-12-28  修订日期:2016-06-10
DOI:
中文关键词: 樟子松  加载速率  能量吸收  缓冲系数
英文关键词: Scotch pine  loading rate  energy absorption  cushioning coefficient
基金项目:国家自然科学基金资助(31300483); 江苏省自然科学基金(BK20130971);江苏高校优势学科建设工程资助
作者单位
江向东 南京林业大学南京 210037 
徐朝阳 南京林业大学南京 210037 
李健昱 南京林业大学南京 210037 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究樟子松在不同静态径向加载速率作用下的能量吸收特性。 方法 采用横纹径向压缩实验。 结果 在不同加载速率的作用下,应力-应变曲线都呈现出 3 个阶段,即弹性阶段,应力平台阶段以及密实化阶段。樟子松存在明显的应变速率敏感性,随着加载速率的增加,应力-应变曲线的应力平台阶段不断上升。当应变为 0.06,加载速率为 1 mm/min 时,应力为 4.38 MPa; 当加载速率为 10 和 30mm/min 时,对应的应力分别为 4.71 和 6.56 MPa。樟子松具有优良的吸能能力,其能量吸收效率可以达到 0.7~0.8。其缓冲系数曲线呈“L”型,随着应变的增加缓冲系数不断减小,但受加载速率的影响不大。 结论 不同加载速率对樟子松的能量吸收特性有一定的影响。
英文摘要:
      This work aimed to study the Scotch pine energy absorption characteristics under the effect of different radial Static loading rate. Across-compression radial tests were carried out. Under different loading rates, the stress-strain curves showed three stages: elastic stage, stress stage and densification stage. There was obvious strain rate sensitivity of Scotch pine, with the increase of loading rate, the plateau stage of stress-strain curves rose gradually. At the strain rate of 0.06, the loading rate was 1 mm/min, the stress was 4.38 MPa; When the loading rates was 10 mm/min and 30 mm/min, the corresponding stress was 4.71 MPa and 6.56 MPa, respectively. Scotch pine had excellent energy absorption capacity, the energy absorption efficiency of samples could reach 0.7~0.8. The cushioning coefficient curves of the samples were "L" type, and the cushioning coefficient curves decreased with the increase of the strain, but the load rate had little effect. The energy absorption capacity of wood was influenced by different loading rates.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20790669位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号