姜方园,卢立新,邱晓琳,唐亚丽.环化SBS吸氧共混物的制备及其性能研究[J].包装工程,2015,36(23):58-61.
JIANG Fang-yuan,LU Li-xin,QIU Xiao-lin,TANG Ya-li.Preparation and Property of Cyclized Styrene-butadiene Oxygen Scavenging Blend[J].Packaging Engineering,2015,36(23):58-61.
环化SBS吸氧共混物的制备及其性能研究
Preparation and Property of Cyclized Styrene-butadiene Oxygen Scavenging Blend
投稿时间:2015-05-24  修订日期:2015-12-10
DOI:
中文关键词: SBS  环化SBS  吸氧
英文关键词: SBS  cyclized SBS  oxygen scavenging
基金项目:
作者单位
姜方园 江南大学无锡 214122 
卢立新 1. 江南大学无锡 2141222. 江苏省食品先进制造装备技术重点实验室无锡 214122 
邱晓琳 1. 江南大学无锡 2141222. 江苏省食品先进制造装备技术重点实验室无锡 214122 
唐亚丽 1. 江南大学无锡 2141222. 江苏省食品先进制造装备技术重点实验室无锡 214122 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 制备环化SBS吸氧共混物并对其性能进行研究。方法 以苯乙烯-丁二烯共聚物(SBS)为原料, 在对甲苯磺酸的催化作用下, 制备苯乙烯-丁二烯共聚物环化物 (环化SBS)。将环化SBS与引发剂、 过渡金属催化剂共混制备环化SBS吸氧共混物, 经紫外光照射引发吸氧反应从而吸收氧气。研究环化SBS吸氧共混物的吸氧性能, 以及吸氧反应对吸氧共混物结构与性能的影响。结果 吸氧共混物的吸氧量在第4天时就达到30.7 mL/g, 随着时间的延长, 吸氧量继续增加, 在第10天时基本达到平衡,最大吸氧量为40.2 mL/g。环化SBS经紫外光照射引发吸氧后生成醇类物质, 吸氧后环化SBS吸氧共混物的拉伸强度与断裂伸长率均略有降低, 但是变化不显著。结论 试验制备的环化SBS吸氧共混物具有良好的吸氧性能, 可用于制备单层/多层吸氧薄膜。
英文摘要:
      Cyclized SBS oxygen scavenging blend was prepared and its properties were studied. The cyclized styrene-butadiene triblock copolymer (cyclized SBS) was prepared with styrene-butadiene triblock copolymer (SBS) as raw material and p-toluene sulphonic acid as catalyst. The oxygen scavenging blend was prepared by blending cyclized SBS, photoinitiator, and transition metal catalyst, triggering oxygen scavenging reaction after UV irradiation. The oxygen scavenging property and the effects of oxygen scavenging reaction on the structure and properties of oxygen scavenging blend were studied. The oxygen scavenging quantity achieved 30.7 mL/g on the fourth day. The O2 uptake continued to increase over time, and became generally balanced on the tenth day. After oxygen scavenging reaction, cyclized SBS was oxidized into alcohols. The tensile strength and the elongation at break of the blend film slightly decreased after oxygen scavenging, but the changes were not significant. In conclusion, the oxygen scavenging blend prepared in this work has good oxygen scavenging performance, and can be used to prepare single-layer/multi-layer oxygen scavenging film.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20817641位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号