储信庆,计宏伟.灰底白板纸与白卡纸的弹性常数对比[J].包装工程,2015,36(23):48-52.
CHU Xin-qing,JI Hong-wei.Comparison of the Elastic Constants between the Gray Manila Board and Ivory Board[J].Packaging Engineering,2015,36(23):48-52.
灰底白板纸与白卡纸的弹性常数对比
Comparison of the Elastic Constants between the Gray Manila Board and Ivory Board
投稿时间:2015-07-20  修订日期:2015-12-10
DOI:
中文关键词: 数字图像相关方法  灰底白板纸  白卡纸  泊松比  弹性模量
英文关键词: digital image correlation method  gray manila board  ivory board  Poisson′ s ratio  Young′ s modulus
基金项目:天津市应用基础与前沿技术研究计划重点项目 (14JCZDJC34600)
作者单位
储信庆 天津商业大学天津 300134 
计宏伟 天津商业大学天津 300134 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 为了更加精确地测量灰底白板纸和白卡纸的泊松比和弹性模量。方法 将数字图像相关方法与单向拉伸实验相结合。通过对灰底白板纸和白卡纸试样拉伸变形前后的图像进行分析, 测量其泊松比; 通过对灰底白板纸和白卡纸的力-位移曲线进行分析, 测量其弹性模量。结果 测得了定量为300, 400 g/m2的灰底白板纸的泊松比分别为0.281和0.245, 其弹性模量分别为154.47, 226.06 MPa;300, 400 g/m2的白卡纸的泊松比分别为 0.312 和 0.276, 其弹性模量分别为 209.09, 297.79 MPa。结论同种类别的纸张中, 定量越高, 其弹性模量越大, 而泊松比越小; 在定量相同的情况下, 白卡纸的泊松比和弹性模量都比灰底白板纸的大。
英文摘要:
      The aim of this work was to accurately measure the Poisson′ s ratio and Young′ s modulus of gray manila board and ivory board. The combination of digital image correlation method (DICM) and tensile test was used in this paper. The Poisson′ s ratio was measured by analyzing the images of the gray manila board and ivory board specimens before and after tensile deformation. And the Young′ s modulus was measured by analyzing the force-displacement curves of gray manila board and ivory board. The Poisson′ s ratio for gray manila board with ration of 300 and 400 g/m2 was 0.281 and 0.245, respectively, and the Young′ s modulus was 154.47 and 226.06 MPa, respectively. The Poisson′ s ratio for ivory board with ration of 300 and 400 g/m2 was 0.312 and 0.276, respectively, and the Young′ s modulus was 209.09 and 297.79 MPa, respectively. The higher ration corresponded to the higher Young′ s modulus and the lower Poisson′ s ratio for the same category of board. In the case of the same ration, the Young′ s modulus and Poisson′ s ratio of ivory board were higher than those of the gray manila board.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20820383位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号