王彤,钱怡.缓蚀型玉米秸秆纤维发泡包装材料的研究[J].包装工程,2015,36(3):1-5,14.
WANG Tong,QIAN Yi.Corrosion-inhibiting and Cushioning Packaging Materials of Corn Straw Stalk Fiber[J].Packaging Engineering,2015,36(3):1-5,14.
缓蚀型玉米秸秆纤维发泡包装材料的研究
Corrosion-inhibiting and Cushioning Packaging Materials of Corn Straw Stalk Fiber
投稿时间:2014-11-03  修订日期:2015-02-10
DOI:
中文关键词: 玉米秸秆纤维  气相缓蚀剂  缓冲材料  纤维发泡材料
英文关键词: corn stalk fiber  volatile corrosion inhibitor  cushioning material  fiber foam material
基金项目:
作者单位
王彤 江南大学无锡 214122 
钱怡 1. 江南大学无锡 2141222. 国家轻工业包装制品质量监督检测中心无锡 214122 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 制备并研究缓蚀型玉米秸秆纤维发泡包装材料的性能。方法 以廉价环保易得的玉米秸秆纤维、 废纸纤维和气相缓蚀剂为原料, 添加适量的成膜剂、 胶黏剂、 发泡剂、 交联剂等, 以微波发泡的方式制备玉米秸秆纤维缓蚀缓冲包装材料。对材料的静态缓冲性能进行测试分析, 得到此缓冲材料缓冲性能的基本特征, 通过密闭空间定量评价方法对材料的缓蚀性能进行测定。结果 微波发泡不仅使材料存在较多的储能空间而且缓蚀效果增强, 添加由二甲基咪唑啉、 尿素和硼砂以质量比4∶1∶2复配的缓蚀剂后, 发泡材料的缓蚀效果可达90%以上, 而不添加缓蚀剂的纤维发泡材料会加速金属腐蚀。结论 此发泡材料具有良好的缓冲性能与缓蚀性能, 基于目前的研究进展, 提出了通过改变发泡剂和粘合剂用量达到对缓蚀剂进行控释的构想。
英文摘要:
      To prepare and study a new type of environment friendly volatile corrosion inhibition (VCI) packaging material and its characteristics. The light, environment friendly and inexpensive waste paper fiber, corn straw stalk fiber and volatile corrosion inhibitor were chosen as raw materials. After addition of appropriate amount of film-forming agent, adhesive, foaming agent and crosslinker, the corrosion-inhibiting and cushioning packaging material of corn straw stalk fiber was produced using the microwave foaming method. The static cushioning properties of the material was tested and analyzed in order to get the basic cushioning characteristics of the cushioning materials. The corrosion inhibition ability was tested by the confined space quantitative evaluation method. Microwave foaming did not only provide the material with more storage space, but also enhanced the corrosion inhibition properties. After addition of corrosion inhibitor made of PDMBI, carbamide and borax compounded with the ratio of 4 ∶ 1 ∶ 2, the corrosion inhibition rate of the foaming fiber materials reached more than 90%, while the fiber foaming material without VCI accelerated metal corrosion. The foamed material had good cushioning and corrosion inhibition properties. In addition, based on the research progress, this paper put forward that the release of corrosion inhibitor might be controlled by changing the dosage of foaming agent and adhesive.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20817397位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号